Materia structura
Usus summus qualitas admisceatur ferro ut matrix, per specialem superficiem infiltrationis curationis et technologiae processus, resistentia et anti morsu exercitii peractae traditionis mixturae ferri caloris tractatae gestus adhuc meliore sunt, at friction signanter minuendo coefficientem. Peculiaris structura designationis superficiei oleum cycli copia multum extendit.
|  CSB-260 vexillum oleum cisternina |  CSB-262 Iusto reticulum oleum cisternina |  CSB-265 Oleum regulae foraminis |
| Technical Parameter |
| Model | CSB260 | CSB262 | CSB265 |
| Maximum Lond | Static adferentem facultatem | 250Mpa | 300Mpa | 300Mpa |
| Dynamic onus afferentem | 100Mpa | 100Mpa | 150Mpa |
| Maxime linearibus velocitas | lubrication | 10m/min | 15m/min | 30m/min |
| Maximum PV valorem | lubrication | 1.5N/mm²*m/s | 2.0N/mm²*m/s | 2.5N/mm²*m/s |
| Fensity | 7.8g/cm³ | 7.8g/cm³ | 7.8g/cm³ |
| Superficiem duritiem | ≥550 HV1 | ≥550 HV1 | ≥550 HV1 |
| Scelerisque expansion coefficientes | 1.1×10*℃ | 1.1×10*℃ | 1.x10*℃ |
| Frictio coefficientis | lubrication | 0.05~0.2 | 0.05~0.2 | 0.05~0.2 |
| Usus temperatus | -40℃- 250℃ | -40℃- 250℃ | -40℃- 250℃ |
| Matching axis | asperitas | Ra<0.8 | Ra<0.8 | Ra<0.8 |
| duritia | HRC 58-62 | HRC 58-62 | HRC 58-62 |
| Commendatur lubrication temporis intervallum | <50hr | 50-100hr | 250hr |
| Sede fovea commendatur: H7. Shaft 17 |
Typical applications
Explicatio huius generis intendit proposita reponere ferrum caloris traditi tractatum secundum gestus illapsum, ut sumptus sustentationem reducere, lubricationis impensas, et veteres abnormes induere in usu. Applicationes typicae sunt machinae portus, machinae silvae, machinamenta machinamenta, axes salsissimus, logistics instrumenta et alia cylindrica oleum aurium frutices, gestus articulatos..